李建保
材料与化工学院
职称：教授
作者：ZHIBO YAO，YE ZHANG，HEPING SHEN，JIANBAO LI，KUNIHITO KOUMOTO，HONG LIN （State Key Laboratory of New Ceramics & Fine Processing,School of Materials Science and Engineering,Tsinghua University；Key Laboratory of Ministry of Education for Advanced Materials in Tropical Island Resources,Hainan University；Department of Applied Chemistry,Graduate School of Engineering,Nagoya University）
出处：第一届新型太阳能电池暨钙钛矿太阳能电池学术研讨会 2014
摘要：Perovskite-sensitized solar cells were fabricated in the air using sequential deposition technique, for which a key step is spin-coating the solution ...
作者：Panneng Qian，Shiwei Lin，Jianbao Li （Key Laboratory of Ministry of Education for Advanced Materials in Tropical Island Resources, School of Materials and Chemical Engineering, Hainan University, Haikou 570228, Hainan, China）
出处：第五届世界氢能技术大会 2013
关键词：hydrogen；production；photocatalysis；TiO2；nanotube；arrays；crystal；structures
发明人：邓湘云，白成英，李建保，冯家迪，景亚妮，苏魁范，王春鹏，蒋文凯，廖昕星，张国庆
申请日期：2012.12.04
摘要：本发明公开了一种复合碳化硅陶瓷纤维过渡层的涂覆方法，包括以下步骤：支撑体干压成型后，预烧结。在支撑体表面上利用空气喷涂技术均匀涂覆一层莫来石纤维和硅酸铝纤维的混合料;干燥后在其表面上流延一层过滤膜，最后将制成的碳化硅过滤膜材料坯体进行烧结，即可得复合碳化硅过滤膜材料。本发明可以制备均匀完整，厚度可控 ...
作者：陈永，李玲，洪玉珍，李建保，陈润六 （海南大学海南优势资源化工材料应用技术教育部重点实验室,硅锆钛资源综合开发与利用海南省重点实验室）
出处：材料导报 2011
关键词：椰壳纤维；热分解；动力学
摘要：将椰壳纤维在NaOH、KOH、ZnCl2和(NH4)2HPO4溶液中进行处理,并采用耐驰STA449C-Jupiter同步热分析仪研究了椰壳纤维在不同升温速率时的热分解反应。通过积分法对椰壳纤维的热解失重曲线进行动力学分析发现,升温速率为5K/min时热解的主反应阶段的活化能最低,低温段和高温段的分 ...
被引情况：超星被引 7 次作者：Luo Songping，Lin Hong，Gu Youchen，Liu Chenyang，Li Jianbao （State Key Laboratory of New Ceramics and Fine Processing ,School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China；State Key Laboratory of New Ceramics and Fine Processing ,School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China；College of Materials Science and Chemical Engineering, Hainan University, Haikou 570228, China）
出处：第一届新型太阳能电池暨钙钛矿太阳能电池学术研讨会 2014
关键词：reduced；graphene；oxide；PEDOT-PSS；hybrid；films；transparent；conductive；films
摘要：Chemical reduction of graphene oxide can be used to produce large quantities of reduced graphene oxide for potential application in electronics, optoe ...
作者：ZHIBO YAO，YE ZHANG，HEPING SHEN，JIANBAO LI，KUNIHITO KOUMOTO，HONG LIN （State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China；State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China；Key Laboratory of Ministry of Education for Advanced Materials in Tropical Island Resources, Hainan University, Haikou, China；Department of Applied Chemistry, Graduate School of Engineering, Nagoya University, Furo-cho Chikusa-ku, Nagoya 464-8603, Japan）
出处：第一届新型太阳能电池暨钙钛矿太阳能电池学术研讨会 2014
关键词：Perovskite；Solar；Cell；PbI2；Concentration；Photoluminescence-quenching
作者：邱文达，邓湘云，李建保 （海南大学材料与化工学院；海南优势资源化工材料应用技术教育部重点实验室 海口570228；天津师范大学物理与电子信息学院 天津300387；清华大学材料科学与工程系 北京100084）
出处：硅酸盐通报 2011
关键词：火山岩；砖；结构；性能
摘要：以火山岩、粉煤灰、炉底渣等工业固体废弃物为原料，通过添加一些添加剂，采用压制成型方法，制备了高性能的墙砖。采用XRD、SEM测试技术分别对样品的相组成和显微结构进行了分析，并测量了样品的吸水率、气孔率、体积密度及抗压强度。结果表明，经合理烧结后的样品的主晶相为钙长石、蓝晶石、高岭土、钠长石、氧化铁、 ...
被引情况：超星被引 1 次作者：吴新正，邓湘云，李建保，陈缔，马振强 （海南大学材料与化工学院海南优势资源化工材料应用技术教育部重点实验室硅锆钛资源综合开发与利用海南省重点实验室；天津师范大学物理与电子信息学院；清华大学材料科学与工程系新型陶瓷与精细工艺国家重点实验室）
出处：绝缘材料 2010
关键词：石英砂；高硅陶瓷；干燥
摘要：研究了干燥制度对石英砂制高硅陶瓷坯体性能影响,采用DSC/TG研究了试样干燥过程中能量和质量的变化。分析了坯体的干燥过程,以及温度、升温速率和保温时间等因素对陶瓷坯体性能的影响。研究表明,高硅陶瓷坯体以10℃/min升温速率,达到120℃后保温2 h,其物理性能最佳。
被引情况：超星被引 6 次作者：葛世荣，李建保，柳振万，杨金廷 （中国矿业大学；海南大学；大连外国语学院党委；邯郸学院）
出处：教育与职业 2010
关键词：教育品牌；办学理念；大学校长；海南大学；高等教育强国；大学教师；品牌建设；品牌战略；中国矿业大学；大学品牌
摘要：主持人：万祎 投稿邮箱：amelie_van@yahoo．com.cn 以品牌战略建设行业特色性大学 葛世荣 中国矿业大学校长 未来10年是中国建设创新型国家和高等教育强国的关键时期，中国高等教育在规模上目前在世界上排名绝对第一，但是还没有世界一流品牌的大学，从办学的 ...
被引情况：超星被引 2 次作者：朱素娟，陈永，肖伟龙，张海涛，邓湘云，李建保，邱文达，章文 （海南优势资源化工材料应用技术教育部重点实验室硅锆钛资源综合开发与利用海南省重点实验室海南大学材料与化工学院；天津师范大学物理与电子信息学院；清华大学材料科学与工程学院新型陶瓷与精细工艺国家重点实验室）
出处：陶瓷学报 2011
关键词：多孔陶瓷；烧结温度；保温时间；孔隙率；断裂强度
摘要：以石英砂为主要原料,采用液相烧结法,经半干压成型制备石英质多孔陶瓷。采用SEM对多孔陶瓷的显微结构进行表征。探讨了烧结温度、保温时间对多孔陶瓷孔隙率及断裂强度的影响。结果表明:随着烧结温度升高,保温时间延长,石英质多孔陶瓷的孔隙率下降、断裂强度不断增大;最佳烧结温度为1250℃,最佳保温时间为30m ...
被引情况：超星被引 9 次